Pipe Grades

Pipe Grade

Polyethylene pipe grade is a type of high-density polyethylene (HDPE) specifically designed for manufacturing pressure pipes used in the transportation of water, gas, and industrial fluids. It offers high strength, good flexibility, excellent chemical resistance, and a long service life, making it an ideal material for modern piping systems.

Black PE Compound

Property	Test Method	Unit	Value
MFI (2.16kg,190°C)	ISO 1133-1	g/10 min	≤0.2
Density	ISO 1183-1	g/cm3	1.5±0.2
Carbon Black Content	ISO 6964	%	15±3
Ash Content	ISO 3451	%	35±5
OIT (200°C)	ISO 11357-6	Min	≥20
Volatile Content	EN 12099	ppm	≤350

Black PE 80 Compound

Property	Test Method	Unit	Value
MFI (5kg,190°C)	ISO 1133-1	g/10 min	055 ± 0.15
Density	ISO 1183-1	g/cm3	0.954 ± 0.005
Carbon Black Content	ISO 6964	%	2.25 ± 0.25
Carbon Black Dispersion	ISO 18553	Grade	≤ 3
OIT (200°C)	ISO 11357-6	Min	≥25
Volatile Content	EN 12099	ppm	≤350

Blue HDPE PE 100 Compound

Property	Test Method	Unit	Value
MFI (5kg,190°C)	ISO 1133-1	g/10 min	026 ± 0.05
Density	ISO 1183-1	g/cm3	0.950 ± 0.005
Volatile Content	EN12099	ppm	≤ 300
OIT (200°C)	ISO 11357-6	min	≥ 30
Tensile Strength at Yield	ISO 6259-1,3	Mpa	≥22
Elongation at Break	ISO 6259-1,3	%	≥500
Internal Pressure Resistance -At 20°C, 12 Mpa -At 80°C, 5,4 Mpa -At 80°C, 5 Mpa	ISO 1167	Hours	>100 >165 >1000

Yello HDPE for Gas Pipe Stripes

Property	Test Method	Unit	Value
MFI (5kg,190°C)	ISO 1133-1	g/10 min	025 ± 0.05
Density	ISO 1183-1	g/cm3	>0.945
Tensile Strength at Yield	ISO 6259-1,3	Mpa	≥21
Elongation at Break	ISO 6259-1,3	%	≥400
Vicat softening point (1Kg)	ISO 306	°C	134 ±1
Vicat softening point (5Kg)	ISO 306	°C	85 ±1
Melting Point (DSC Method )	ISO 11357-1	°C	133
Volatile content	EN 12099	ppm	≤350
Internal Pressure Resistance -At 20°C, 12 Mpa -At 80°C, 5,4 Mpa -At 80°C, 5 Mpa	ISO 1167	Hours	>100 >165 >1000
OIT -AT 210°C -AT 200°C	ISO 11357-6	Min	≥25 ≥50
Heat Deflection Temp (HDT) -AT 1.8 Mpa ( Method A ) -AT 8 Mpa ( Method C )	ISO 75-1	°C	55 ±1 43 ±1